Dental composites, including glass ionomer cement (GIC), have been successfully used in dentistry. However, they have mainly been used for teeth under weak loads or in areas requiring aesthetic factors because of their low bonding strength, polymerization shrinkage, and low biocompatibility. In this study, carbonate anions were applied to ethyl 2-cyanoacrylate (EC) to improve the physical properties of the composite, and the strength, curing time, and setting time were tested according to different concentrations. Furthermore, the shear bonding strength was measured against that of dentin, and biocompatibility was determined based on the viability of fibroblasts. The optimum concentration of sodium bicarbonate (SBC) in cyanoacrylate was 11 mol%, and its compressive strength was approximately 1.3 times that of pure EC. Furthermore, EC–SBC showed higher biocompatibility and 1.4 times higher bonding strength than GIC. Therefore, EC–SBC can be widely used in dental adhesive restorations.

글라스 아이오노머 시멘트(GIC)를 비롯한 치과용 복합재는 치과 분야에서 널리 사용되고 있습니다. 그럼에도 불구하고 낮은 결합력, 중합 수축, 재료의 생체 적합성이 상대적으로 낮아 하중이 낮게 걸리는 치아 부분 또는 미적 요소가 필요한 치아에 주로 사용되어 왔습니다. 본 연구에서는 복합재의 물성을 향상시키기 위해 탄산 음이온을 에틸 2-시아노아크릴레이트(EC)에 적용하고, 이들 농도에 따른 결합 강도, 경화 시간, 가동 시간에 대해 테스트했습니다. 또한 상아질에 대한 전단 결합 강도를 측정하고 섬유아세포의 생존력에 따라 생체 적합성을 결정했습니다. 시아노아크릴레이트 내 중탄산나트륨(SBC)의 최적 농도는 11 mol% 였으며 압축 강도는 순수 EC에 비해 약 1.3배 높았습니다. 또한 EC-SBC는 GIC에 비해 1.4배 높은 결합 강도를 나타냈으며 좋은 생체 적합성을 보였습니다. 따라서 EC-SBC 소재는 치과용 접착제 및 치아 복원용 접착제 분야에 널리 적용될 수 있습니다.

Keywords: cyanoacrylate, sodium bicarbonate, reinforced composite, dental composite, bioglue.