Blends of poly(ether imide) (PEI) and bisphenol-A polycarbonate (PC) have been investigated by differential scanning calorimetry (DSC) and scanning electron microscopy(SEM). Blends were prepared by screw extrusion with weight fractions of PEI in the blends varying from 0.90 to 0.10. From the measured glass transition temperature (T_g) and the apparent weight fractions of PEI and PC dissolved in each phase, it appears that PC dissolves more in the PEI-rich phase than does the PEI in the PC-rich phase. The values of the Flory-Huggins polymer-polymer interaction parameter were determined and found to be from 0.198 to 0.271 for blends at 310℃. The interaction parameter decreases with increasing PEI concentration. This result is consistent with the inclination of T_g values and the microscopy study which shows that compatibility increases more in the PEI-rich compositions than in the PC-rich compositions.

Poly(ether imide) (PEI)와 bisphenol-A polycarbonate (PC)의 블렌드를 시차 주사 열분석기(DSC)와 주사 전자 현미경(SEM)을 이용하여 열적 성질과 모폴로지를 관찰하였다. 블렌드 시편은 PEI의 무게조성을 0.9에서 0.1까지 0.1씩 변화시키면서 스크류 압출기를 이용하여 제조하였다. DSC를 이용하여 측정된 블렌드의 유리 전이 온도(T_g) 결과로부터 PEI-PC 블렌드의 각 상에 녹아있는 PEI 및 PC 각각 성분의 겉보기 무게 분율(apparent weight fraction)을 계산하였다. 이 결과로부터 PEI를 많이 포함하고 있는 상(PEI-rich phase)에 녹아 있는 PC의 양이 PC를 많이 포함하고 있는 상(PC-rich phase)에 녹아 있는 PEI의 양보다 많음을 알 수 있었다. Flory-Muggins식을 이용하여 PEI와 PC의 상호 작용 계수(χ₁₂)를 계산하였으며, 그 결과 χ₁₂는 310℃에서 블렌드 조성에 따라 0.198과 0.271 사이의 값을 가짐을 알 수 있었다. PEI-PC 블렌드 의 χ₁₂는 PEI의 조성이 증가할수록 감소하는 경향을 나타내었다. 주사 전자 현미경을 이용하여 PEI-PC 블렌드의 모폴로지를 관찰한 결과 PC가 많이 포함된 조성보다는 PEI가 많이 포함된 조성에서 상용성이 증가하는 결과를 볼 수 있었다. 이 결과는 유리 전이 온도를 이용하여 구한 PEI-PC 블렌드의 χ₁₂와도 일치함을 알 수 있었다.

Keywords: poly(ether imide); polycarbonate; blend; interaction parameter; compatibility